Anomalous phase transition and ionic conductivity of AgI nanowire grown using porous alumina template

Changhao Liang*, Kazuya Terabe, Tsuyoshi Hasegawa, Masakazu Aono, Nobuo Iyi

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

24 Citations (Scopus)


Silver-iodide (AgI)-based superionic conductors are attracting widespread interest for their potential applications in electrochemical devices such as sensors and batteries. A new kind of nanocomposite with highly ordered AgI nanowires embedded in an anodic-aluminum-oxide (AAO) membrane was fabricated by low-temperature step-electrochemical growth. Structural evolution, phase transition, and ionic conductivity were investigated by x-ray diffraction, differential scanning calorimetry, and impedance measurements. The phase transition from Βγ-AgI phase to α-AgI phase occurred at temperature of 168 °C, that is, higher than that of reported bulk AgI (147 °C); abnormally, the α to Βγ phase-transition temperature on cooling was also depressed as large hysteresis formed. The high-temperature phase, namely, α-AgI, remained at temperatures as low as 80 °C. The initial highly oriented-growth AgI nanowire disappeared after undergoing heating and cooling processes and a mixture of polycrystalline Βγ-AgI and amorphouslike interface phases formed. The cooled AgI-AAO composite displayed ionic conductivity in the order of 10-2 S cm-1 at room temperature. This array-structured nanocomposite of AgI-AAO may be further developed for usage as a new type of battery, i.e., "nanobatteries" and " nanosensors" with individual AgI nanowires as basic elements.

Original languageEnglish
Article number124308
JournalJournal of Applied Physics
Issue number12
Publication statusPublished - 2007
Externally publishedYes

ASJC Scopus subject areas

  • Physics and Astronomy(all)


Dive into the research topics of 'Anomalous phase transition and ionic conductivity of AgI nanowire grown using porous alumina template'. Together they form a unique fingerprint.

Cite this