Influence of melting temperature on morphology of primary mullite in SiO2-Al2O3 system

H. Nakae*, S. Nakano, M. Yoshida

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

9 Citations (Scopus)


A series of melting and solidification experiments were carried out using high-purity SiO2 and Al2O3 powders as the starting materials. The effect of melting temperature on the morphology of the primary mullite was investigated. The following conclusions were made: 1) The morphology of the primary mullite went through five stages as the melting temperature increased; massive, fibrous, faceted dendritic, feathery and fine feathery structures. These phenomena can be explained based on the number of effective nuclei in the melt. 2) The fibrous mullite grew from mullite precursors formed in the melt. Under highly supercooled conditions, the fibrous morphology becomes unstable and begins to branch and form a faceted dendritic crystal. 3) When the number of nuclei is extremely small, the mullite nucleated on the rhombic dodecahedron Mo originating from the molybdenum crucible and crystallizes out into a feathered structure.

Original languageEnglish
Pages (from-to)1163-1169
Number of pages7
JournalMaterials Transactions, JIM
Issue number9
Publication statusPublished - 1995

ASJC Scopus subject areas

  • Engineering(all)


Dive into the research topics of 'Influence of melting temperature on morphology of primary mullite in SiO2-Al2O3 system'. Together they form a unique fingerprint.

Cite this