Structure and magnetic properties of pulse-plated FeP and FeCuP amorphous alloys

K. Kamei*, Y. Maehara

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

11 Citations (Scopus)


FeP and FeCuP alloys have been prepared by pulsed galvanostatic electrodeposition from a sulphuric acid solution. A current pulse, with a height of 100 mA cm-2 and on and off time durations of 100 ms, was found to be most effective for the formation of FeP amorphous alloy. The composition range of the plating solution giving an amorphous structure was wider for pulse plating than for direct current plating. Most of the pulse-plated amorphous alloys contained about 20 at.% P and their lowest coercive force (Hc) was about 0.2 Oe. The pulse-plated FeCuP ternary alloy was deposited even at a high pulse current density of 1 A cm-2. The alloy formed at 300 mA cm-2 showed the lowest Hc of 0.5 Oe. Cross-sectional scanning electron microscopy examination of the pulse-plated FeCuP alloy revealed a very fine multilayered structure.

Original languageEnglish
Pages (from-to)906-910
Number of pages5
JournalMaterials Science and Engineering A
Issue numberC
Publication statusPublished - 1994 May 15
Externally publishedYes

ASJC Scopus subject areas

  • General Materials Science


Dive into the research topics of 'Structure and magnetic properties of pulse-plated FeP and FeCuP amorphous alloys'. Together they form a unique fingerprint.

Cite this