Temporal Evolution of Microscopic Structure and Functionality during Crystallization of Amorphous Indium-Based Oxide Films

Junjun Jia*, Shimpei Iwasaki, Shingo Yamamoto, Shin Ichi Nakamura, Eisuke Magome, Toshihiro Okajima, Yuzo Shigesato

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

9 Citations (Scopus)


Understanding the crystallization mechanism of amorphous metal-oxide thin films remains of importance to avoid the deterioration of multifunctional flexible electronics. We derived the crystallization mechanism of indium-based functional amorphous oxide films by using in situ X-ray diffraction (XRD) and transmission electron microscopy (TEM) measurements. Crystallization begins with surface nucleation, especially at low annealing temperatures, and proceeds simultaneous nucleation and growth in the bulk. Three-dimensional crystal growth in the film was observed when the crystallite size was sufficiently smaller than the film thickness. When the growing crystallites reached the film surface, the crystallization was dominated by two- or lower-dimensional growth. Such crystallization can be explained within the framework of the modified Avrami theory and can be varied for tailoring the electrical properties of the amorphous In2O3 film. After tailoring the film crystallinity and crystallite size, the carrier mobility was improved to >100 cm2/V·s in 30 min. Our results show that a carrier mobility of >90 cm2/V·s can be implemented for the In2O3 film with a crystallinity of >40% and a crystallite size of >70 nm by an optimized annealing process. The incorporation of Ga element into amorphous In2O3 films obviously increases the activation energy of nucleation and migration. In contrast, Sn dopants can promote the crystal growth. This is attributed to two kinds of migration mechanisms during the annealing in air, one of which is the dominant migration mechanism of oxygen interstitials in crystallized indium-tin oxide (ITO) films and the other dominated by oxygen vacancies in In2O3 and IGO films. Combining the modified Avrami theory with TEM observations, we predicted the structural evolution kinetics for indium-based amorphous oxide films and gained new insights for understanding the temporal structure-functionality relationship during crystallization.

Original languageEnglish
Pages (from-to)31825-31834
Number of pages10
JournalACS Applied Materials and Interfaces
Issue number27
Publication statusPublished - 2021 Jul 14


  • Avrami theory
  • ITO films
  • InO
  • carrier mobility
  • crystal growth
  • crystallization
  • functional amorphous oxides
  • oxygen migration mechanism

ASJC Scopus subject areas

  • Materials Science(all)


Dive into the research topics of 'Temporal Evolution of Microscopic Structure and Functionality during Crystallization of Amorphous Indium-Based Oxide Films'. Together they form a unique fingerprint.

Cite this