Anion exchange membranes containing no β-hydrogen atoms on ammonium groups: Synthesis, properties, and alkaline stability

Daniel Koronka, Kenji Miyatake*


研究成果: Article査読

4 被引用数 (Scopus)


Novel anion conductive polymer membranes have been designed and synthesized to investigate whether the absence of β-hydrogen atoms of ammonium groups affects the membranes' properties and chemical stability. The hydrophilic monomer, 2,2-bis(4-chlorobenzyl)-2-phenyl-ethylamine (3), was obtained via a two-step reaction with an overall yield of 98% under mild reaction conditions. Ni(0)-promoted copolymerization of 3 with 2,2-bis(4-chlorophenyl)hexafluoropropane (1) afforded high molecular weight copolymers (Mn = 12.8-19.6 kDa, Mw = 82.1-224.6 kDa). After quaternization with iodomethane, QBAF-BS polymers formed bendable, robust membranes from solution casting. The ion exchange capacity (IEC) of the membranes ranged from 1.50 to 2.44 mequiv. g-1. The membranes exhibited high hydroxide ion conductivity in water (up to 191 mS cm-1 at 80 °C for IEC = 2.25 mequiv. g-1), suggesting that the newly designed hydrophilic structure was effective in improving the ion conductivity. Based on small-angle X-ray scattering (SAXS) analyses and transmission electron microscopy (TEM) images, all membranes featured nano-phase separated morphology with a large dependence on the copolymer composition. The strain properties were improved on increasing the content of the hydrophilic component up to IEC = 2.25 mequiv. g-1, above which the strain became smaller due to the larger water absorption. The membranes were not stable under harsh alkaline conditions (in 8 M KOH at 80 °C) gradually losing the hydroxide ion conductivity. Compared to our previous AEMs which contained typical aliphatic ammonium groups, the lack of β-hydrogen atoms did not practically improve the alkaline stability of AEMs possibly due to the main chain degradation but contributed to higher ion conductivity.

ジャーナルRSC Advances
出版ステータスPublished - 2020 12月 16

ASJC Scopus subject areas

  • 化学 (全般)
  • 化学工学(全般)


「Anion exchange membranes containing no β-hydrogen atoms on ammonium groups: Synthesis, properties, and alkaline stability」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。