Flame-synthesized (CoO)x(Al2O3)1-x spinel nanopowders with primary particles of ∼20 nm were used to grow small diameter carbon nanotubes (CNTs). The nanopowders with x ≤ 0.35 grew few CNTs whereas that with x = 0.65 grew CNTs efficiently. Low crystalline and large-diameter multi-wall CNTs grew by annealing and chemical vapor deposition (CVD) at 800 °C for ∼10 min, whereas single-wall CNTs with high crystallinity (G-band to D-band intensity ratio of 20–100 by Raman spectroscopy) grew by annealing and CVD at ≥1000 °C for ∼10 s. The excess Co in the spinel reduced and segregated to form multiple Co nanoparticles on the surface of the single primary alumina nanoparticles in ∼10 s, yielding SWCNTs in ∼10 s. Such flame synthesized nanopowders, reduced and activated by H2, provide CNTs from C2H2, all in ten-second time scale, and as such are promising for practical, high-through-put production of small-diameter CNTs.