Consolidation of hydrogenation-disproportionation-desorption-recombination processed Nd-Fe-B magnets by spark plasma sintering

K. Suresh; T. Ohkubo; Y. K. Takahashi; K. Oh-ishi; R. Gopalan; K. Hono; T. Nishiuchi; N. Nozawa; S. Hirosawa

doi:10.1016/j.jmmm.2009.07.010

Consolidation of hydrogenation-disproportionation-desorption-recombination processed Nd-Fe-B magnets by spark plasma sintering

K. Suresh, T. Ohkubo, Y. K. Takahashi, K. Oh-ishi, R. Gopalan, K. Hono^*, T. Nishiuchi, N. Nozawa, S. Hirosawa

^*この研究の対応する著者

研究成果: Article › 査読

23 被引用数 (Scopus)

抄録

We have successfully consolidated hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-Co-Zr-B-Ga powder by spark plasma sintering (SPS). The field compacted samples were sintered at different temperatures (T_S) from 550 to 600 °C with compressive pressure of 80 MPa for 20 min. Microstructural investigations by transmission electron microscopy indicated that the sintered specimen exhibits Nd₂Fe₁₄B grains of ~300 nm with Nd-rich grain boundary phase. The optimum magnetic properties of B_r: 1.22 T, H_c: 928 kA/m, _BH_c: 600 kA/m, (BH)_max: 210 kJ/m³ were obtained in the sample sintered at 550 °C. The strategy for further improving the coercivity and remanence is discussed based on the microstructure-property relationships.

本文言語	English
ページ（範囲）	3681-3686
ページ数	6
ジャーナル	Journal of Magnetism and Magnetic Materials
巻	321
号	22
DOI	https://doi.org/10.1016/j.jmmm.2009.07.010
出版ステータス	Published - 2009 11月
外部発表	はい

ASJC Scopus subject areas

電子材料、光学材料、および磁性材料
凝縮系物理学

文献へのアクセス

10.1016/j.jmmm.2009.07.010

他のファイルとリンク

フィンガープリント

「Consolidation of hydrogenation-disproportionation-desorption-recombination processed Nd-Fe-B magnets by spark plasma sintering」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル

@article{6111fc4525454ada9fd6816b465ccb83,

title = "Consolidation of hydrogenation-disproportionation-desorption-recombination processed Nd-Fe-B magnets by spark plasma sintering",

abstract = "We have successfully consolidated hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-Co-Zr-B-Ga powder by spark plasma sintering (SPS). The field compacted samples were sintered at different temperatures (TS) from 550 to 600 °C with compressive pressure of 80 MPa for 20 min. Microstructural investigations by transmission electron microscopy indicated that the sintered specimen exhibits Nd2Fe14B grains of ~300 nm with Nd-rich grain boundary phase. The optimum magnetic properties of Br: 1.22 T, Hc: 928 kA/m, BHc: 600 kA/m, (BH)max: 210 kJ/m3 were obtained in the sample sintered at 550 °C. The strategy for further improving the coercivity and remanence is discussed based on the microstructure-property relationships.",

keywords = "Coercivity, HDDR, Nd-Fe-B, Permanent magnet, Spark plasma sintering",

author = "K. Suresh and T. Ohkubo and Takahashi, {Y. K.} and K. Oh-ishi and R. Gopalan and K. Hono and T. Nishiuchi and N. Nozawa and S. Hirosawa",

year = "2009",

month = nov,

doi = "10.1016/j.jmmm.2009.07.010",

language = "English",

volume = "321",

pages = "3681--3686",

journal = "Journal of Magnetism and Magnetic Materials",

issn = "0304-8853",

publisher = "Elsevier",

number = "22",

}

TY - JOUR

T1 - Consolidation of hydrogenation-disproportionation-desorption-recombination processed Nd-Fe-B magnets by spark plasma sintering

AU - Suresh, K.

AU - Ohkubo, T.

AU - Takahashi, Y. K.

AU - Oh-ishi, K.

AU - Gopalan, R.

AU - Hono, K.

AU - Nishiuchi, T.

AU - Nozawa, N.

AU - Hirosawa, S.

PY - 2009/11

Y1 - 2009/11

N2 - We have successfully consolidated hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-Co-Zr-B-Ga powder by spark plasma sintering (SPS). The field compacted samples were sintered at different temperatures (TS) from 550 to 600 °C with compressive pressure of 80 MPa for 20 min. Microstructural investigations by transmission electron microscopy indicated that the sintered specimen exhibits Nd2Fe14B grains of ~300 nm with Nd-rich grain boundary phase. The optimum magnetic properties of Br: 1.22 T, Hc: 928 kA/m, BHc: 600 kA/m, (BH)max: 210 kJ/m3 were obtained in the sample sintered at 550 °C. The strategy for further improving the coercivity and remanence is discussed based on the microstructure-property relationships.

AB - We have successfully consolidated hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-Co-Zr-B-Ga powder by spark plasma sintering (SPS). The field compacted samples were sintered at different temperatures (TS) from 550 to 600 °C with compressive pressure of 80 MPa for 20 min. Microstructural investigations by transmission electron microscopy indicated that the sintered specimen exhibits Nd2Fe14B grains of ~300 nm with Nd-rich grain boundary phase. The optimum magnetic properties of Br: 1.22 T, Hc: 928 kA/m, BHc: 600 kA/m, (BH)max: 210 kJ/m3 were obtained in the sample sintered at 550 °C. The strategy for further improving the coercivity and remanence is discussed based on the microstructure-property relationships.

KW - Coercivity

KW - HDDR

KW - Nd-Fe-B

KW - Permanent magnet

KW - Spark plasma sintering

UR - http://www.scopus.com/inward/record.url?scp=69549106001&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=69549106001&partnerID=8YFLogxK

U2 - 10.1016/j.jmmm.2009.07.010

DO - 10.1016/j.jmmm.2009.07.010

M3 - Article

AN - SCOPUS:69549106001

SN - 0304-8853

VL - 321

SP - 3681

EP - 3686

JO - Journal of Magnetism and Magnetic Materials

JF - Journal of Magnetism and Magnetic Materials

IS - 22

ER -