抄録
The purpose of this study is to clarify corrosion mechanism of a duplex stainless steel (DSS) through dissolution behavior of a ferritic phase and austenitic phase, respectively. A single phase specimen ([α] or [γ] phase specimen) which has chemical composition of each phase of a DSS was prepared by preferential dissolution of the DSS, and dissolution behavior of each phase specimen was investigated. The [α] specimen showed a less-noble corrosion potential compared to the [γ] specimen. The change of the corrosion potential of the DSS was located somewhere between those of each phase specimen. The [α] specimen showed a less-noble active peak compared to the [γ] specimen. The current density value of the DSS was located between the current values of each phase specimen. It was clearly shown that the corrosion mechanism of a DSS could be described through the dissolution behavior of single phases such as α phase and γ phase.
| 本文言語 | English |
|---|---|
| ホスト出版物のタイトル | ECS Transactions |
| ページ | 17-22 |
| ページ数 | 6 |
| 巻 | 25 |
| 版 | 37 |
| DOI | |
| 出版ステータス | Published - 2010 |
| イベント | Corrosion General Session - 216th ECS Meeting - Vienna 継続期間: 2009 10月 4 → 2009 10月 9 |
Other
| Other | Corrosion General Session - 216th ECS Meeting |
|---|---|
| City | Vienna |
| Period | 09/10/4 → 09/10/9 |
ASJC Scopus subject areas
- 工学（全般）