Fabrication of porous Al-Cu alloys with aligned unidirectional pores by dipping pipes in melt and semi-solid slurry

Tatsuro Hayashida, Shinsuke Suzuki, Junichi Ichikawa, Ryuji Toyoyama

研究成果: Article査読

4 被引用数 (Scopus)

抄録

Aligned seven pure aluminum pipes with internal diameter of 3mm and wall thickness of 0.5mm were dipped into Al4 mass% Cu melt and semi-solid slurry. The specimen was cooled and solidified after holding times 0, 15 and 30 s. The pipes were bonded to the base metal with maintaining the shape of pipes by using the semi-solid base metal. An increase in solid fraction of the base metal is effective to avoid thermal damage of the pipes. Penetration of Cu into the pipe was found by EPMA analyses. Diffusion of Cu from the base metal to grain boundary of pipes decreases the liquidus temperature of ¡ phase in the vicinity of the grain boundary of the pipes. As a result, the ¡ phase melted partly and the pipes were bonded to the pipes with the base metal metallurgically. Porous AlCu alloys with aligned unidirectional pores with porosity of 26% are fabricated by this method.

本文言語English
ページ(範囲)2102-2108
ページ数7
ジャーナルMaterials Transactions
54
11
DOI
出版ステータスPublished - 2013

ASJC Scopus subject areas

  • 材料科学一般
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Fabrication of porous Al-Cu alloys with aligned unidirectional pores by dipping pipes in melt and semi-solid slurry」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル