Formation of PPy/Ta2O5/Ta structure by electropolymerization

Young‐Seo ‐S Park, Shinji Takeoka, Kimihisa Yamamoto, Eishun Tsuchida*


    研究成果: Article査読

    3 被引用数 (Scopus)


    Electropolymerization of pyrrole on tantalum (Ta) electrodes was carried out in buffer solutions (0.04 M phosphoric acid, 0.04 M acetic acid, 0.04 M boric acid and 0.2 M sodium hydroxide) containing 0.1 M sodium ptoluenesulfonate (TsONa) under galvanostatic conditions and it was found that a polypyrrole (PPy) and a tantalum oxide (Ta2O5) layer are formed on a Ta electrode by an electrochemical oxidation process. The conditions of this simultaneous formation were studied in respect to current density (id), pyrrole concentration ([Py]), pH and the amount of electricity. Under certain conditions ([Py] = 0.25 M, pH = 1.8, id = 10–20 mA cm−2, the amount of electricity = 1 C), 6–8 μm thick PPy films were efficiently formed on homogeneous 30–50 nm thick Ta2O5 layers. The PPy film showed a high electrical conductivity (110 s cm−1), adhered well and covered the Ta2O5 layer. The resulting PPy/Ta2O5/Ta system is therefore proved to have excellent properties as a capacitor.

    ジャーナルPolymers for Advanced Technologies
    出版ステータスPublished - 1992

    ASJC Scopus subject areas

    • ポリマーおよびプラスチック


    「Formation of PPy/Ta2O5/Ta structure by electropolymerization」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。