Highly ordered, thermally/hydrothermally stable cubic Ia3d aluminosilica monoliths with low silica in frameworks

Sherif El-Safty*, Ahmed Shahat, Kazuyuk Ogawa, Takaaki Hanaoka


研究成果: Article査読

34 被引用数 (Scopus)


High order aluminosilica monoliths (Al/HOM-5) with cubic Ia3d structures were fabricated with low silica content (Si/Al = 1) by means of a simple, reproducible, and one-pot synthesis strategy. A realistic control over the cubic Ia3d geometry of aluminosilica monoliths was achieved by using microemulsion phases of copolymer P123 (EO20PO70EO20) as soft templates. The textural and geometrical pore structures and acidic properties of Al/HOM-5 were characterized by means of various tools of XRD, N2 isotherms, HRTEM, FTD, FESEM, 27Al and 29Si MAS NMR, EDX, and NH3-TPD. The incorporated amounts of Al species in Al/HOM-5 monoliths play a key determinant in the formation of the coordination state of the aluminum species in four (AlIV, AlO4)-, five (Al V, AlO4)-, and six (AlVI, AlO 6)-coordinate environments. Results show evidence of the formation of aluminosilicas with disordered distribution of Si and Al sites in the frameworks. In addition, the increase of the aluminum contents enhanced the distortion in the pore uniformity of Al/HOM-5 monoliths. The large amount of acid sites was revealed with the high aluminum contents into the pore framework walls. With high-temperature treatments (≥1073 K), the γ-Al 2O3 phase with face-centered-cubic Fd3m symmetry can be formed in the monolithic aluminosilica matrices. This finding might indicate that the dealumination effect at high thermal treatment would be expected to generate many defect sites existing in the Al/HOM-5 frameworks. Accordingly, a large mass transport of aluminum from tetrahedral aluminum (framework) to octahedral aluminum (extra framework) was occurred, leading to form a separate aluminum species into the crystalline alumina matrices. Moreover, cubic Ia3d aluminosilica structures exhibit outstanding steam stability even with high Al content (Si/Al = 1). However, the mesostructured integrity of Al/HOM-5 can be retained under 100% steam treatments with N2 flow for 8 h at 1073 K, permitting their desirability in various applications such as catalysis, adsorption, and sensing technologies.

ジャーナルMicroporous and Mesoporous Materials
出版ステータスPublished - 2011 2月

ASJC Scopus subject areas

  • 材料科学(全般)
  • 材料力学
  • 化学 (全般)
  • 凝縮系物理学


「Highly ordered, thermally/hydrothermally stable cubic Ia3d aluminosilica monoliths with low silica in frameworks」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。