抄録
Superconducting YBCO particles with an average size of 1-2 μm were prepared by dry-type jet mill. It is found from the measurements of critical currents (Ic) that the superconducting transition temperature (Tc) at 91 - 92 K is obtained for the YBCO particles which have oriented and elongated grains align parallel to (003) (005) and (006) -plane. On the other hand, fine YBCO particles were prepared from high quality superconducting YBCO powders by wet - type jet mill in a high pressure flow of MEK (methyl-ethyl-ketone:CH3COCH2CH3) or toluene(C6H5CH3). As a result, the resulting particles are homogenius in MEK and fine YBCO particles show oriented and polycrystal structures with an average particle size of 164nm in diameter and with the lattice parameter of a=3.9A, b=3.5A in [001]-orientation from TEM (Transmission Electron Microscopy) - studies.
| 本文言語 | English |
|---|---|
| ホスト出版物のタイトル | Proceedings of the IEEE International Conference on Properties and Applications of Dielectric Materials |
| Place of Publication | Piscataway, NJ, United States |
| 出版社 | IEEE |
| ページ | 794-796 |
| ページ数 | 3 |
| 巻 | 2 |
| 出版ステータス | Published - 2000 |
| イベント | 6th Interantional Conference on Properties and Applications of Dielectric Materials - Xi'an, China 継続期間: 2000 6月 21 → 2000 6月 26 |
Other
| Other | 6th Interantional Conference on Properties and Applications of Dielectric Materials |
|---|---|
| City | Xi'an, China |
| Period | 00/6/21 → 00/6/26 |
ASJC Scopus subject areas
- 電子工学および電気工学
- 電子材料、光学材料、および磁性材料