title = "Nucleation-type magnetization behavior in FePt (001) particulate films",
abstract = "Nucleation-type magnetization behavior is reported in sputtered FePt (001) films with an island structure, where the particles show a multiple-domain structure. A large coercivity H C of more than 50 kOe is achieved at an initial applied field of only 6 kOe. The magnetization behavior and the magnetic domain observation indicate clearly that domain walls are wiped out completely at a low applied field, and once domain walls are wiped out, it is hard to nucleate reversed domains in the particles, resulting in high H C. The remarkable nucleation-type behavior of magnetization is also found to give rise to anomalous minor loops when the applied magnetic field is alternated around zero and increased gradually.",
author = "T. Shima and K. Takanashi and Takahashi, {Y. K.} and K. Hono and Li, {G. Q.} and S. Ishio",
note = "Funding Information: We thank J. A. C. Bland for a critical reading of this manuscript, S. Sugimoto for a fruitful discussion, and Y. Murakami for his technical assistance. This work was partly supported by the Special Coordination Funds for Promoting Science and Technology on “Nanohetero Metallic Materials” from the Ministry of Education, Culture, Sports, Science and Technology. X-ray-diffraction measurements were performed at the Laboratory for Advanced Materials, IMR, Tohoku University. High-field magnetic measurements were performed at the Center for Low Temperature Science, Tohoku University.",
year = "2006",
month = feb,
day = "1",
doi = "10.1063/1.2169878",
language = "English",
volume = "99",
journal = "Journal of Applied Physics",
issn = "0021-8979",
publisher = "American Institute of Physics Publising LLC",
number = "3",
}