Preparation of anatase phase titanium dioxide film by non-aqueous electrodeposition

Takuma Hachisu, Kazuaki Shi, Tokihiko Yokoshima, Atsushi Sugiyama, Shigeki Kuroiwa, Tetsuya Osaka*, Noriko Nakajima, Masahiro Yoshino


研究成果: Article査読

11 被引用数 (Scopus)


The electrodeposition-annealing route to fabricating thin film of the promising photocatalyst material anatase-titanium dioxide (anatase-TiO2) has been studied. The sample was deposited with a solution of N,N-dimethylformamide containing titanium compound by controlled-potential technique. SEM image showed the annealed sample at 600 °C for 1 h under air provided a continuous film with a thickness of ca. 350 nm. In this sample, X-ray photoelectron spectrum corresponding to the Ti 2p peak assigned to a chemical bond of TiO2 and X-ray diffraction peaks assigned to the anatase phase were observed, respectively. Electrochemical oxidation in sodium sulfate solution on this annealed film was enhanced in the presence of UV light radiation. These results confirm the successful synthesis of photocatalytic anatase-TiO2 film by the electrodeposition and annealing process.

ジャーナルElectrochemistry Communications
出版ステータスPublished - 2016 4月 1

ASJC Scopus subject areas

  • 電気化学


「Preparation of anatase phase titanium dioxide film by non-aqueous electrodeposition」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。