SrS:Ce nanoparticles were prepared using a reverse micelle method and coated by ZnO. The mono-dispersed nanoparticles whose size was as small as 3nm were observed by transmission electron microscope (TEM) and dynamic light scattering (DLS) method. Optical properties of the core-shell SrS:Ce/ZnO nanoparticle was studied. UV-visible absorption and photoluminescence (PL) properties were measured and compared with those of SrS:Ce and SrS nanoparticles. Bright blue photoluminescence (around 440 nm) was observed from SrS:Ce at a room temperature when nanoparticles were excited using a Hg lamp. The PL peak intensity enhancement was observed after forming the ZnO shell. The optical absorption profile of nanoparticles was associated with the band edge feature of SrS. The coating of the SrS:Ce surface by ZnO has affected the electronic structure of SrS:Ce nanoparticles.
| 本文言語 | English |
|---|---|
| 論文番号 | B10.2 |
| ページ（範囲） | 485-489 |
| ページ数 | 5 |
| ジャーナル | Materials Research Society Symposium Proceedings |
| 巻 | 829 |
| 出版ステータス | Published - 2005 6月 20 |
| イベント | Progress in Compound Semiconductor Materials IV - Electronic and Optoelectronic Applications - Boston, MA, United States 継続期間: 2004 11月 29 → 2004 12月 3 |
ASJC Scopus subject areas
- 材料科学（全般）
- 凝縮系物理学
- 材料力学
- 機械工学