Reaction and oxygen permeation studies in Sm_0.4Ba _0.6Fe_0.8Co_0.2O_{3 - δ} membrane reactor for partial oxidation of methane to syngas

A disk-type Sm_0.4Ba_0.6Co_0.2Fe _0.8O_{3 - δ} perovskite-type mixed-conducting membrane was applied to a membrane reactor for the partial oxidation of methane to syngas (CO + H₂). The reaction was carried out using Rh (1 wt%)/MgO catalyst by feeding CH₄ diluted with Ar. While CH₄ conversion increased and CO selectivity slightly decreased with increasing temperature, a high level of CH₄ conversion (90%) and a high selectivity to CO (98%) were observed at 1173 K. The oxygen flux was increased under the conditions for the catalytic partial oxidation of CH₄ compared with that measured when Ar was fed to the permeation side. We investigated the reaction pathways in the membrane reactor using different membrane reactor configurations and different kinds of gas. In the membrane reactor without the catalyst, the oxygen flux was not improved even when CH ₄ was fed to the permeation side, whereas the oxygen flux was enhanced when CO or H₂ was fed. It is implied that the oxidation of CO and H₂ with the surface oxygen on the permeation side improves the oxygen flux through the membrane, and that CO₂ and H ₂O react with CH₄ by reforming reactions to form syngas.