Single-crystal growth of Bi2Sr2Ca2Cu3O10+δ (Bi-2223) by TSFZ method

Takenori Fujii, Takao Watanabe, Azusa Matsuda

研究成果: Article査読

77 被引用数 (Scopus)


The traveling solvent floating-zone (TSFZ) method has the potential advantage over the usual flux method that crystal growth can be performed at one point on the temperature-composition phase diagram, and provides an opportunity to grow large single crystals even if their crystallization field is very narrow. Here, we report the first successful preparation of the triple-layered system Bi2Sr2Ca2Cu3O10+δ (Bi-2223) single crystals by improving the TSFZ method condition by applying slow growth velocity and higher temperature gradient. The obtained crystals are as large as 4×2×0.1 mm3. X-ray diffraction pattern shows only sharp Bi-2223 peaks, confirming its good crystallinity. DC susceptibility of the as-grown samples exhibits a sharp superconducting transition with Tc = 105 K. After annealing the sample under O2 flow at 600 °C, Tc increased to the maximum value (= 110 K). High-resolution transmission electron microscope images were taken to investigate the phase purity. It confirms that the crystals cleaved from the last part of grown boule are almost single-phase Bi-2223.

ジャーナルJournal of Crystal Growth
出版ステータスPublished - 2001 2月

ASJC Scopus subject areas

  • 凝縮系物理学
  • 無機化学
  • 材料化学


「Single-crystal growth of Bi2Sr2Ca2Cu3O10+δ (Bi-2223) by TSFZ method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。