Sorption mechanisms of arsenate in Aqueous solution during coprecipitation with aluminum hydroxide

Daisuke Haraguchi, Chiharu Tokoro*, Yuji Oda, Shuji Owada


研究成果: Article査読

16 被引用数 (Scopus)


This study investigates the removal mechanism of arsenate, i.e., As(V), by coprecipitation with aluminum hydroxide in solution at pH 5. Both the ltrates and precipitates were analyzed. The removal mechanisms of As(V) were investigated by constructing sorption isotherms and by analyses of X-ray diraction (XRD) patterns, zeta potentials, and Fouriertransform infrared (FT-IR) spectra. The sorption isotherms showed Brunauer-Emmett-Teller (BET) behavior. The sorption densities showed a rapid uniform increase when the initial As/Al solution molar ratio was more than 1.5. This suggests two sorption mechanisms of As(V), namely surface complexation and three-dimensional uptake, which were dependent on the initial As/Al molar ratio. It is important to note that the As(V) and Al(III) concentrations were unable to reach the thermodynamic solubility product of aluminum arsenate in the bulk solution. The three-dimensional uptake was therefore estimated to be not bulk precipitation but surface precipitation of aluminum arsenate. Surface precipitation, generation of a new surface phase, is known to be derived from surface complexes. XRD, zeta potential, and FT-IR analyses of the precipitates for each As/Al molar ratio conrmed that As(V) was predominantly removed by the adsorption of the As(V) oxyanions to the aluminum hydroxide surface when the initial As/Al molar ratio was less than 1.5. At an initial As/ Al molar ratio greater than 1.5 at pH 5, As(V) was removed mostly by surface precipitation, evidently by poorly crystalline aluminum arsenate on the surface. This sorption as surface precipitation is a phenomenon specic to the coprecipitation process.

出版ステータスPublished - 2013 2月 1

ASJC Scopus subject areas

  • 化学 (全般)
  • 化学工学(全般)


「Sorption mechanisms of arsenate in Aqueous solution during coprecipitation with aluminum hydroxide」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。