Surface segregation in end fluorinated polystyrenes

R. B. Mason*, C. A. Jalbert, J. F. Elman, Timothy Edward Long, B. Gunesin, J. T. Koberstein


研究成果: Conference article査読

1 被引用数 (Scopus)


Surface segregation effects in a neat system of perfluorinated polystyrenes were investigated using contact angle analysis. Surface composition and surface energies for a homologous series of samples ranging in molecular weight from 5000 g/mol to 100,000 g/mol were determined. The surface enrichment of end groups was found to decrease with increasing molecular weight of PS-F. Calculations show that for the 5000 g/mol PS-F the surface tension was 19.9 mN/m, a massive reduction from 32.4 mN/m for non functional PS and approaching that of PTFE at 18.2 mN/m. The 100,000 PS-F had a surface tension of 29.7 mN/m, an 8% decrease from the non functional polymer for a 0.1% concentration of fluorinated end groups. The molecular weight dependence of polymer surface tension will be compared with theoretical predictions.

ジャーナルAmerican Chemical Society, Polymer Preprints, Division of Polymer Chemistry
出版ステータスPublished - 1998 8月 1
イベントProceedings of the 1997 Boston Meeting - Boston, MA, USA
継続期間: 1998 8月 231998 8月 27

ASJC Scopus subject areas

  • ポリマーおよびプラスチック


「Surface segregation in end fluorinated polystyrenes」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。