Time-dependent dielectric breakdown of atomic-layer-deposited Al2O3 films on GaN

Atsushi Hiraiwa, Toshio Sasaki, Satoshi Okubo, Kiyotaka Horikawa, Hiroshi Kawarada

研究成果: Article査読

19 被引用数 (Scopus)


Atomic-layer-deposited (ALD) Al2O3 films are the most promising surface passivation and gate insulation layers in non-Si semiconductor devices. Here, we carried out an extensive study on the time-dependent dielectric breakdown characteristics of ALD-Al2O3 films formed on homo-epitaxial GaN substrates using two different oxidants at two different ALD temperatures. The breakdown times were approximated by Weibull distributions with average shape parameters of 8 or larger. These values are reasonably consistent with percolation theory predictions and are sufficiently large to neglect the wear-out lifetime distribution in assessing the long-term reliability of the Al2O3 films. The 63% lifetime of the Al2O3 films increases exponentially with a decreasing field, as observed in thermally grown SiO2 films at low fields. This exponential relationship disproves the correlation between the lifetime and the leakage current. Additionally, the lifetime decreases with measurement temperature with the most remarkable reduction observed in high-temperature (450 °C) O3-grown films. This result agrees with that from a previous study, thereby ruling out high-temperature O3 ALD as a gate insulation process. When compared at 200 °C under an equivalent SiO2 field of 4 MV/cm, which is a design guideline for thermal SiO2 on Si, high-temperature H2O-grown Al2O3 films have the longest lifetimes, uniquely achieving the reliability target of 20 years. However, this target is accomplished by a relatively narrow margin and, therefore, improvements in the lifetime are expected to be made, along with efforts to decrease the density of extrinsic Al2O3 defects, if any, to promote the practical use of ALD Al2O3 films.

ジャーナルJournal of Applied Physics
出版ステータスPublished - 2018 4月 21

ASJC Scopus subject areas

  • 物理学および天文学一般


「Time-dependent dielectric breakdown of atomic-layer-deposited Al2O3 films on GaN」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。